Catalyst and process for oxidizing hydrogen sulfide

ABSTRACT

Catalysts comprising bismuth and vanadium components are highly active and stable, especially in the presence of water vapor, for oxidizing hydrogen sulfide to sulfur or SO 2 . Such catalysts have been found to be especially active for the conversion of hydrogen sulfide to sulfur by reaction with oxygen or SO 2 .

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of copending application, Ser. No. 191,864 filed Sept. 29, 1980, which is a continuation-in-part application of Ser. No. 27,033 filed Apr. 4, 1979, now U.S. Pat. No. 4,314,983.

BACKGROUND OF THE INVENTION

This invention relates to a process for oxidizing H₂ S, and particularly to a process for catalytically oxidizing H₂ S to sulfur, SO₂, or both in the presence of a substantial proportion of water vapor.

Current air pollution regulations are very restrictive concerning the amount of H₂ S that may be discharged to the atmosphere. In some instances, gas streams may not be discharged to the atmosphere if they contain more than about 10 ppmv of H₂ S. Thus, many processes have been developed to remove H₂ S from gas streams prior to their discharge to the atmosphere.

One method known in the art for removing H₂ S involves catalytic oxidation, that is, a gas stream containing H₂ S is blended with air or free oxygen, and the resulting mixture is then passed through a bed of catalyst particles under appropriate conditions such that the H₂ S is converted to elemental sulfur vapor or SO₂, or both, as desired. One catalyst useful for the gas phase conversion of H₂ S to sulfur or SO₂ is disclosed in U.S. Pat. No. 4,092,404; it comprises one or more vanadium oxides or sulfides supported on a refractory oxide such as alumina or silica-alumina. Another reference, U.S. Pat. No. 4,012,486, discloses a process wherein a catalyst having active components consisting of bismuth is used to catalytically incinerate H₂ S to SO₂.

When compared, the bismuth catalyst of U.S. Pat. No. 4,012,486 will generally be found less active than the vanadia catalyst of U.S. Pat. No. 4,092,404 for oxidizing H₂ S to SO₂. On the other hand, a bismuth catalyst is much more stable than a vanadia catalyst at operating temperatures below about 600° F. when H₂ S must be removed from a gas stream, such as an off-gas derived from a geothermal power plant, which contains water vapor at a water vapor partial pressure above 1.0 p.s.i.a., usually at least 4.0 p.s.i.a. In general, vanadia catalysts have satisfactory stability in the presence of water vapor at partial pressures below about 1.0 p.s.i.a. or at operating temperatures above about 600° F., but under the combined conditions of temperature below 600° F., and water vapor partial pressures above about 1.0 p.s.i.a., and particularly at 1.5 p.s.i.a., or above, vanadia catalysts deactivate rapidly. It is believed that the reason for this deactivation is due to a complex series of chemical reactions involving the conversion of the vanadium oxide or sulfide active catalytic components to less active forms of vanadium, such as vanadyl sulfate (VOSO₄).

As stated above, vanadia catalysts are highly active for the oxidation of H₂ S and, as disclosed in U.S. Pat. No. 4,243,647, such catalysts have proven most useful for oxidizing H₂ S to sulfur by reaction with either oxygen or SO₂. In the presence of less than about 1.0 p.s.i.a. water vapor, vanadia catalysts have proven to be remarkably stable, providing high conversions of H₂ S to sulfur for a time period of more than one year with little if any deactivation being noticed. But because vanadia catalysts have also been found to be subject to deactivation when the water vapor partial pressure of the gases in contact therewith exceeds 1.0 p.s.i.a., with the rate of deactivation generally increasing with increasing water vapor partial pressure above 1.0 p.s.i.a., it is an object of the invention to improve the deactivation resistance of vanadium-containing catalysts for the oxidation of H₂ S to SO₂ or elemental sulfur in the presence of water vapor at partial pressures of 1.0 p.s.i.a. or more. And despite the high activity of vanadia catalysts for oxidizing H₂ S to SO₂ or sulfur, it is yet another object to provide a vanadium-containing catalyst of substantially improved activity for oxidizing H₂ S to SO₂ or sulfur. It is an additional object of the invention to achieve the foregoing objects while minimizing both the formation of SO₃ and the oxidation of components such as H₂, CO, NH₃, and CH₄ that might also be present during the catalytic oxidation of H₂ S to SO₂ or sulfur. Other objects and advantages will become apparent from the following description of the invention.

SUMMARY OF THE INVENTION

It has now been found that catalysts comprising bismuth and vanadium components are highly active for the gas phase oxidation of hydrogen sulfide to sulfur dioxide or elemental sulfur. In addition, catalysts comprising vanadium and bismuth remain catalytically stable (i.e., resist deactivation) for oxidizing H₂ S to SO₂ or elemental sulfur in the presence of water vapor, and, in one embodiment of the invention, the oxidation of H₂ S to sulfur or SO₂ is catalytically promoted in a reaction zone wherein the operating temperature is below 600° F. and the water vapor partial pressure is above about 1.0 p.s.i.a. In this embodiment of the invention, the water vapor may initially be present in the gases contacted with the catalyst at a partial pressure above about 1.0 p.s.i.a., or, because the oxidation of H₂ S produces an equivalent volume of water, the water vapor partial pressure may initially be below 1.0 p.s.i.a. but increase above about 1.0 p.s.i.a. during contact with the catalyst.

An advantage in the invention resides in the highly selective nature of the catalyst. Operating conditions are readily found for oxidizing H₂ S to sulfur and/or SO₂ while at the same time minimizing the oxidation of such components as H₂, CO, NH₃, and saturated hydrocarbon gases containing no more than 6 carbon atoms (i.e., light hydrocarbons). Additionally, the oxidation of H₂ S to sulfur and/or SO₂ without producing essentially any SO₃ is attainable, even at operating temperatures up to about 900° F. And even when conditions of excess oxygen above that for the conversion of H₂ S to SO₂ are employed, the catalyst is useful for selectively promoting the conversion to the desired product while leaving H₂, CO, NH₃, and light hydrocarbons essentially unoxidized and/or while preventing the formation of a substantial amount of SO₃.

All references herein to catalysts containing vanadium and bismuth or to catalysts containing vanadium and bismuth components include within their meaning catalysts active for oxidizing H₂ S containing (1) elemental vanadium and elemental bismuth, (2) elemental vanadium and one or more bismuth compounds, (3) elemental bismuth and one or more vanadium compounds, (4) one or more compounds and one or moe bismuth compounds, (5) one or more compounds of bismuth and vanadium (e.g., a bismuth vanadate), or (6) a combination of any of the foregoing.

DETAILED DESCRIPTION OF THE INVENTION

Active catalysts for use in the invention comprise vanadium and bismuth as the essential active components. The essential active components may be present as the elements V and Bi, or as a mixture of individual vanadium and bismuth compounds (for example, Bi₂ S₃ admixed with V₂ S₅), or as a compound of both bismuth and vanadium, such as Bi(VO₃)₃, BiVO₄, Bi₂ O₃.V₂ O₅, or Bi₄ (V₂ O₇)₃. Alternatively, the catalyst may contain any combination of elements and compounds of vanadium and bismuth as the essential active components. Preferred catalysts contain at least one vanadium oxide or sulfide (e.g., V₂ O₅, V₂ O₃, V₂ S₅, and V₂ S₃) and at least one bismuth oxide or sulfide (e.g., BiO, Bi₂ O₃, Bi₂ O₅, BiS, Bi₂ S₃, and Bi₂ O₄).

The typical catalyst contains vanadium and bismuth components in an intimate mixture, and although the catalyst may consist essentially of such a mixture, it is highly preferred that the vanadium and bismuth components be composited, as by impregnation or comulling, with a carrier material. The carrier (or support) material usually comprises a porous refractory oxide, including, for example, such preferred refractory oxides as alumina, silica, zirconia, titania, magnesia, silica-alumina, silica-zirconia, silica-titania, silica-magnesia, silica-zirconia-titania, and combinations thereof. Sutiable refractory oxides include acidic metal phosphates and arsenates, such as aluminum phosphate, boron phosphate, aluminum arsenate, chromium phosphate, etc. Other suitable supports include the hydrophobic, crystalline silicas, such as the silicalites taught in U.S. Pat. No. 4,061,724. (As used herein, a refractory oxide is hydrophobic if it is capable of absorbing no more than about 0.5 cc of water per gram.) Also suitable are the amorphous and crystalline aluminosilicate zeolites, whether naturally occurring or synthetically made. The most useful crystalline aluminosilicate zeolites are ion-exchanged so as to remove essentially all ion-exchangeable alkali or alkaline earth components. Of particular usefulness are the crystalline aluminosilicate zeolites which are hydrophobic and essentially free of alkali and alkaline earth components. Illustrative of such zeolites are the ZSM-5 zeolite disclosed in U.S. Pat. No. 3,702,886, the ZSM-11 zeolite disclosed in U.S. Pat. No. 3,709,979, and the several hydrophobic zeolites disclosed in U.S. Pat. No. 4,019,880. Such zeolites are characterized by high ratios of silica to alumina.

One highly preferred refractory oxide carrier is silica-alumina when the alumina is present in a proportion of at least 10 weight percent, preferably between about 20 and 30 weight percent. Catalysts prepared from such supports are usually more active for oxidizing H₂ S than are catalysts prepared with many other refractory oxides. In addition, these silica-alumina supports are highly resistant to sulfation, that is, in the presence of SO₃ and/or SO₂ plus O₂, they are resistant to the formation of aluminum sulfate and the consequent loss of surface area, crushing strength, and activity. In general, it can be expected that catalysts prepared from silica-alumina supports containing at least 10 weight percent alumina will experience little if any deactivation due to sulfation under the process conditions hereinafter described.

Another highly preferred support is alumina, especially gamma alumina. Although alumina is subject to deactivation due to sulfation, alumina-supported vanadium-bismuth catalysts are more active catalytically for oxidizing H₂ S than comparable catalysts containing silica-alumina. Thus, in situations wherein the concern is for the highest possible activity regardless of sulfation effects, alumina presents an advantage over silica-alumina. In particular, alumina supports are often utilized in instances wherein the temperature of the feed gas is insufficient for ignition of H₂ S with silica-alumina supports but not with alumina supports. For example, feed gases laden not only with H₂ S but also with high proportions of water vapor, such as many geothermal steam-derived gases containing 90% or more by volume steam, require a relatively high temperature before ignition commences with silica-alumina supports, and rather than preheating such feed gases to a high ignition temperature, it is usually far more desirale to select a more active alumina-supported catalyst requiring either no preheating of the feed gas or substantially less than that required for a comparable silica-alumina-supported catalyst.

When gas streams containing relatively large proportions of water vapor are to be treated with a catalyst prepared from alumina, silica-alumina, or other porous support materials, it is preferred that the catalyst have pore size characteristics preventing capillary condensation of water in a substantial number of the pores. In general, porous catalysts typically utilized in the invention have mean pore diameters greater than about 50 angstroms, and such catalysts, as well as many catalysts of mean pore diameter below 50 angstroms, are useful in environments wherein the water vapor partial pressure is less than about 75% of the saturation pressure. However, when the water vapor partial pressure increases above about 75% of the saturation pressure, capillary condensation of liquid water in the pores of the catalyst may interfere to an undesirable extent with the diffusion of H₂ S and oxidant reactants to the catalytic active sites within the pores. These detrimental effects of capillary condensation may be reduced by either lowering the water vapor partial pressure, increasing the operating temperature, or increasing the size of the pores, and in many instances, it is most convenient to prepare the catalyst with a porous support suited to the water environment than to raise the operating temperature or remove water in a contact condenser or other separation means. To this end, it has been determined by calculation that pores having diameters of 200 angstroms or greater will not encounter significant capillary condensation if the water vapor is present at a partial pressure no greater than about 95% of the saturation pressure. Similarly, pores of 80 angstroms diameter or greater will not encounter a significant amount of capillary condensation at water vapor partial pressures up to about 88% of the saturation pressure. Accordingly, a substantial number of the pores in a catalyst having a mean pore diameter of 200 angstroms or more will remain free of liquid water at water vapor partial pressures up to at least 95% of saturation while a mean pore diameter of 80 angstroms or more yields a similar result up to 88% of the saturation pressure.

There are several methods known in the art by which vanadium and bismuth components may be composited with a refractory oxide support. One such method involves impregnation, that is, a suitable support, such as pellets or extrudates of 75% SiO₂ -25% Al₂ O₃ silica-alumina, is contacted with a solution of ammonium vanadate (or other soluble vanadium compound), dried at an elevated temperature (usually about 230° F.), and then contacted with a solution of a bismuth salt, such as an acidic solution of a bismuth nitrate or chloride. The composite may also be prepared by any of a variety of comulling techniques. A typical procedure involves mulling silica-alumina with solid ammonium metavanadate, solid bismuth nitrate, and sufficient water to create a paste suitable for extrusion through a die. More preferably, either or both of the vanadium and bismuth salts may be added to the mulling mixture in solutin form. In a preferred embodiment, a mixture of silica-alumina, a solution of bismuth nitrate in dilute nitric acid, and an aqueous solution of ammonium metavanadate are comulled. Alternatively, a silica-alumina or other refractory oxide is comulled, for example, with an ammonium metavanadate solution, then dried or calcined at an elevated temperature, and then comulled with an aqueous solution of a bismuth salt, such as a solution of bismuth nitrate in dilute nitric acid. Comulling may also be accomplished by mixing silica-alumina with one or more bismuth vanadates in the presence of water. Alternatively still, the composite may be prepared by a combination of impregnation and comulling techniques, as by impregnating silica-alumina with ammonium vanadate, calcining, and then comulling with an acidic solution of bismuth nitrate or chloride.

After a composite is prepared by one of the foregoing impregnation and/or comulling methods or their equivalents, the composite is calcined, usually at a temperature between about 700° and about 1600° F., preferably 900° to 1200° F. Calcination produces a catalyst containing vanadium and bismuth largely in the form of the oxides thereof, but the 700° to 1600° F. calcination may also produce sufficient bismuth vanadate, usually in the form of monoclinic bismuth orthovanadate (BiVO₄), to be detected by X-ray diffraction analysis. Bismuth orthovanadate and other bismuth vanadates are often produced even when impregnation or comulling is accomplished without the deliberate addition of a bismuth vanadate. For example, when silica-alumina is comulled (as in Example I hereinafter) with ammonium metavanadate, then further comulled with an acidic solution of bismuth nitrate, extruded, cut into particulate form, and then calcined at 900° to 1000° F., the final product was found to contain sufficient bismuth orthovanadate to be detected by X-ray diffraction analysis.

Finished catalysts herein should contain at least 5.0 weight percent of vanadium and 5.0 weight percent of bismuth, calculated as V₂ O₅ and Bi₂ O₃, respectively. It has been found that catalysts containing less than 5.0 weight percent of either metal, while more active or stable than catalysts containing either vanadium components or bismuth components alone, are somewhat less active and less stable than catalysts containing at least 5.0 weight percent of each component. Preferably, the catalysts contains between 5 and 15 weight percent of each component, but it may contain higher proportions, for example, up to about 20 weight percent, even up to 40 weight percent of each component. Such increased metal loadings, however, are not necessary and usually provide little if any advantage over catalysts containing 15 percent or less of each metal. A highly preferred catalyst, for example, contains between about 7 and 15 weight percent vanadium as V₂ O₅ and between about 8 and 15 weight percent bismuth as Bi₂ O₃, with the most highly preferred catalyst containing at least 8.0 weight percent vanadium components as V₂ O₅ and at least 10 weight percent bismuth components as Bi₂ O₃. (All calculations herein with respect to the proportions of active metal components on the catalyst are reported as the weight percent of vanadium and bismuth as V₂ O₅ and Bi₂ O₃, respectively. Thus, a catalyst particle weighing 5 grams and containing elemental vanadium, elemental bismuth, bismuth sulfide (Bi₂ S₃), vanadium sulfide (V₂ S₅), and bismuth orthovanadate (BiVO₄), each in a weight of 0.1 grams, contains vanadium components in a proportion of 5.52 weight percent as V₂ O₅ and bismuth components in a proportion of 5.48 weight percent as Bi₂ O₃.)

The following two Examples demonstrate preferred procedures for preparing catalysts useful in the invention.

EXAMPLE I

Four hundred twenty-one grams of 75% SiO₂ -25% Al₂ O₃ silica-alumina, commercially sold by the Davison Chemical Division of W. R. Grace & Co. as high alumina cracking catalyst, were placed in a steel muller to which was added 44.2 grams of ammonium metavanadate (NH₄ VO₃) and 6 grams of powdered methylated cellulose. The mixture was mulled for 45 minutes. A solution was then prepared by dissolving 88.8 grams of bismuth nitrate (Bi(NO₃)₃.5H₂ O) in a liquid consisting of 200 cc. water and 32 cc. concentrated nitric acid. The solution was added to the previously mulled mixture, and mulling was continued for 15 minutes. An extrudable paste was then formed by mulling with 71 cc. of water for 15 minutes. The resulting paste was then extruded through a 1/8 inch diameter die and cut into particles having lengths between about 1/8 and 1/2 inch. The extrudates were then allowed to dry overnight at 230° F. The extrudates were then calcined in the presence of air at 932° F. for 2 hours. The resulting catalyst contained 9.1 weight percent vanadium components (as V₂ O₅) and 11.2 weight percent bismuth components as Bi₂ O₃. The catalyst contained an X-ray detectable proportion of bismuth orthovanadate.

EXAMPLE II

Sufficient ammonium metavanadate (NH₄ VO₃) was mulled with the high alumina silica-alumina described in the preceding Example so that, after extrusion and cutting into 1/8 inch diameter by 1/16-1/2 inch cylindrical extrudates and calcination at a temperature of about 932° F. for 2 hours in air, the resulting product contained 10 weight percent vanadium components as V₂ O₅. One hundred grams of such product were then contacted with a solution prepared by dissolving 35 grams of bismuth nitrate (Bi(NO₃)₃.5H₂ O) in a mixture of 100 cc. water and 15 cc. concentrated nitric acid to which was added sufficient water to provide a solution of 120 cc. volume. The solution was allowed to contact the extrudate material for two hours to insure full impregnation. The extrudate material was then filtered, dried overnight at 230° F., and calcined at 932° F. for two hours in the presence of air. The resulting catalyst contained an X-ray detectable proportion of bismuth orthovanadate and further contained 8.63 weight percent vanadium components as V₂ O₅ and 11.6 weight percent bismuth components as Bi₂ O₃.

Catalysts prepared by the foregoing methods or their obvious equivalents have been found to be highly active for the gas phase oxidation of H₂ S to either SO₂, sulfur, or some percentage combination of both, as desired. In addition, such catalysts are remarkably stable in the presence of water vapor. Unlike vanadia catalysts, which are subject to deactivation when oxidizing H₂ S at temperatures below 600° F. and in the presence of water vapor at partial pressures of more than about 1.0 p.s.i.a., vanadium-bismuth catalysts prove highly resistant to deactivation when oxidizing H₂ S to sulfur and/or SO₂ in the presence of substantial water vapor, regardless of operating temperature. For example, the life of preferred vanadium-bismuth catalysts for oxidizing H₂ S at temperatures below about 600° F. and in the presence of water vapor at partial pressures ranging between about 1.5 and 10.0 p.s.i.a. is often at least 90 days, usually at least one year.

The present invention therefore provides an advantage over vanadia catalysts when H₂ S must be oxidized in the presence of water vapor at partial pressures above about 1.0 p.s.i.a., and the catalyst of the inventon has been successfully used to treat a number of feed gases containing H₂ S and water vapor. In one experiment, a vanadium-bismuth catalyst proved useful for converting H₂ S to elemental sulfur by reaction with oxygen at a temperature of about 380° F. in the presence of water vapor at a partial pressure of about 9.0 p.s.i.a. In another, it was found that an alumina-supported vanadium-bismuth catalyst, containing about 10% by weight of each metal, calculated as V₂ O₅ and Bi₂ O₃, respectively, resisted deactivation even in the presence of water vapor at partial pressures exceeding 50 p.s.i.a. More specifically, essentially no deactivation resulted at 332° F. and 20,000 GHSV when H₂ S, present in a concentration between 320 and 345 ppmw, was incinerated from a geothermal gas stream also containing water vapor at a partial pressure greater than 60 p.s.i.a. and a concentration by volume greater than 95 percent.

In addition, vanadium-bismuth catalysts are highly selective when oxidizing H₂ S, conditions being readily found for converting H₂ S to sulfur and/or SO₂ at operating temperatures up to 900° F. without substantial formation of SO₃, even in the presence of excess oxygen. The catalyst is also selective for oxidizing H₂ S in the presence of H₂, CO, NH₃, and light hydrocarbons. It has been found, for example, when non-condensable gases obtained from geothermal steam, consisting essentially of 16.7 volume percent H₂, 1.4 volume percent H₂ S, 12.7 volume percent CH₄, 38.8 volume percent CO₂, 4.4 volume percent O₂, 16.0 volume percent N₂, and 10.0 volume percent water, were subjected to incineration conditions of 3600 v/v/hr space velocity and varying temperatures between about 590° and 780° F. in the presence of a catalyst consisting essentially of 9.7 weight percent vanadium components, calculated as V₂ O₅, and 11.2 weight percent bismuth components, calculated as Bi₂ O₃, on a 75% SiO₂ -25% Al₂ O₃ support, that essentially full conversion of H₂ S to SO₂ is achieved without oxidizing essentially any methane while about 5% of the hydrogen was oxidized at a temperature of 590° F. and about 10% at 670° F. At higher temperatures, hydrogen consumption increased with increasing temperature, methane consumption remained nil, and essentially no SO₃ was formed.

The choice as to whether or not the H₂ S in a given gas stream is to be converted to elemental sulfur or SO₂ will most likely depend upon local air pollution regulations. Typically, the maximum concentration of H₂ S allowable for discharge to the atmosphere is about 10 ppmv while SO₂ may be discharged in a maximum concentration varying between about 500 ppmv and 2.0 vol.%. Hence, incineration, i.e., conversion of H₂ S to SO₂, will usually be directed to gas streams containing between about 10 ppmv and 2.0 vol.% H₂ S, while the typical gas stream treated for conversion to elemental sulfur will contain at least about 500 ppmv H₂ S, usually 500 ppmv to 10.0 vol.% H₂ S, preferably 500 ppmv to 5.0 vol.% H₂ S, and most preferably 500 ppmv to 2.0 vol.% H₂ S.

Normally, the gas streams treated in the process of the invention contain, in addition to H₂ S, any of such components as N₂, CO₂, CO, H₂, SO₂, O₂, Ar, NH₃, H₂ O, and light hydrocarbons. Typical gas streams for treatment herein include such H₂ S-containing gas streams as sour natural gases, off-gases derived from geothermal stream, and high temperature, gasified coal or gasified residual oil. The gas stream may also contain such sulfur-containing components as COS, CS₂, and light mercaptans (i.e., saturated mercaptans containing no more than six carbon atoms). If such sulfur-containing components are present, it is preferred that the gas stream be pretreated by the process disclosed in U.S. Pat. No. 3,752,877, herein incorporated by reference. According to this process, CS₂, COS, and light mercaptans, along with SO₂ if present, are simultaneously converted at elevated temperatures (usually 300° to 900° F.) to H₂ S by reaction with H₂ and/or water vapor in the presence of a catalyst comprising one or more active catalytic components of Co, Mo, Fe, W, Ni, with combinations of Co with Mo or Ni with Mo being most preferred. The pretreated gas stream will then contain H₂ S as essentially the only gaseous sulfur component and may be treated by a process described herein so that the H₂ S may be converted to SO₂ and/or elemental sulfur as desired.

A gas stream especially suited to the foregoing pretreatment method is a Claus tail gas. Other gas streams which are preferably pretreated prior to contact with the catalyst of the invention are those containing olefins or aromatics. Olefins deactivate the catalyst herein by forming gums that deposit on the catalyst surfaces, and aromatics such as benzene, when present in significant proportions, e.g., 100 ppmv, deactivate the catalyst when the operating temperature is below about 350° F. Both types of deactivation, however, are only temporary, the olefin deactivation being overcome by high temperature oxidation of the gum-containing catalyst and the aromatics deactivation by raising the operating temperature above 350° F. Alternatively and more preferably, gas streams containing aromatic or olefin components are pretreated so as to remove these deleterious components prior to contact with the catalyst of the invention. One such pretreatment method, particularly suitable for gas streams containing olefins, is catalytic hydrogenation under the conditions and with the catalyst hereinbefore specified for gas streams containing SO₂, CS₂, COS, and light mercaptans.

Gas streams to be treated by incineration should either contain sufficient oxygen or be blended with sufficient oxygen or air so as to provide at least the stoichiometric proportion required for:

    2H.sub.2 S+3O.sub.2 →2SO.sub.2 +2H.sub.2 O.         (I)

More preferably, oxygen is present in a proportion in excess of stoichiometric, usually in a proportion between about 1.1 and 2.5 times the stoichiometric proportion. Other conditions usually employed in incinerating H₂ S in an adiabatic or isothermal reactor include (a) operating pressures between about 5 and 500 psia, with pressures of 15-75 psia being preferred, (b) inlet operating temperatures in the range of 250°-900° F., with temperatures below about 600° F. and especially below about 450° F. being preferred, and (c) space velocities between 100 and 50,000 v/v/hr, with 500-5000 v/v/hr being preferred. Operating conditions are appropriately adjusted so that at least 90% of the H₂ S is incinerated to SO₂. Preferably, the operating conditions are adjusted so that essentially all the H₂ S is incinerated. Conditions known to produce essentially full conversion of H₂ S to SO₂ include: 450° F., 50 psig, 2000 v/v/hr (gas volume calculated at 60° F.), 2.2 times the stoichiometric proportion of air, and 2700 ppmv H₂ S in the feed gas. The following Example III demonstrates the suitability of these conditions.

EXAMPLE III

A feed gas stream having a composition shown in Table I was blended at a rate of 460 scc/min (gas volume measured at 60° F.) with water vapor fed at a rate of 40 scc/min and air fed at the rate of 19.8 scc/min. The resultant gas mixture, having a water vapor content of 7.7 vol.% and an oxygen content of about 0.80 vol.% (2.23 times stoichiometric) was then passed for 15 days at a pressure of 50 psig, a constant temperature of 450° F., and a space velocity of about 2000 v/v/hr through an isothermal catalytic reactor containing 15 cc. of catalyst particles comprising 11.6 weight percent bismuth components (as Bi₂ O₃) and 8.6 weight percent vanadium components (as V₂ O₅). The catalyst was prepared as described in Example II, and the water partial pressure within the reactor was about 5.0 psia. The product gas was analyzed on the 15th day by appropriate mass spectrometrical techniques, and the results are reported on an anhydrous basis in Table I. As shown, the H₂ S was completely converted to SO₂, and no H₂ or methane was oxidized. The SO₃ content of the effluent gas was determined to be from 3 to 5.0 ppm.

                  TABLE I                                                          ______________________________________                                                    Feed Composition                                                                          Product Composition                                      ______________________________________                                         Hydrogen     873     ppmv     838    ppmv                                      Methane      1.68    vol. %   1.60   vol. %                                    Nitrogen     0       ppmv     2.77   vol. %                                    Oxygen       0       ppmv     0.43   vol. %                                    Argon        3       ppmv     365    ppmv                                      Carbon Dioxide                                                                              97.96   vol. %   94.85  vol. %                                    Hydrogen Sulfide                                                                            2717    ppmv     0      ppmv                                      Methyl Mercaptan                                                                            2       ppmv     0      ppmv                                      Carbonyl Sulfide                                                                            4       ppmv     0      ppmv                                      Sulfur Dioxide                                                                              36      ppmv     2212   ppmv                                      Carbon Disulfide                                                                            0       ppmv     0      ppmv                                      Total Sulfur Com-                                                                           2759    ppmv     2212   ppmv                                      pounds as SO.sub.2.sup.1                                                       ______________________________________                                          .sup.1 Note:                                                                   The reason a lower concentration of total sulfur compounds was found in        the product gas than in the feed was due to dilution by the blend of air       oxidant and also by the fact that on the 15th day of operation the H.sub.      S concentration in the feed was somewhat lower than shown in Table I.    

EXAMPLE IV

Six differently prepared catalysts were tested under the conditions of Example III to determine how active and stable they were for incinerating H₂ S in the presence of 5.0 psia water vapor pressure. The six catalysts were prepared as follows:

10 weight percent V₂ O₅ on silica-alumina

A mixture of ammonium vanadate and the high alumina cracking catalyst described in Example I were mulled in the presence of sufficient water to create a paste suitable for extrusion. The paste was extruded through a 1/8 inch die, cut into pieces about 1/16-1/2 inch in length, dried at 230° F., and calcined in air at 932° F. for two hours. The catalyst consisted of 10 weight percent vanadium components (calculated as V₂ O₅) and silica-alumina (75% silica-25% alumina).

36.6 weight percent V₂ O₅ on silica-alumina

One hundred and eight grams of ammonium metavanadate, 291 grams of the high alumina silica-alumina described in Example I, and 7.74 grams of methylated cellulose were mulled in the presence of sufficient water to produce an extrudable paste. The paste was then extruded and cut into 1/8 inch diameter by 1/16-1/2 inch long cyclindrical pieces. The extrudates were dried overnight at 230° F. and calcined at 932° F. for two hours in the presence of air. The catalyst so produced contained 36.6 weight percent vanadium components (calculated as V₂ O₅) on silica-alumina (75% SiO₂ -25% Al₂ O₃).

10.2 weight percent Bi₂ O₃ on alumina

This catalyst was prepared according to a method similar to that taught in Example I of U.S. Pat. No. 4,012,486. The procedure utilized was as follows: 17 gm BiCl₃ was dissolved in 40 cc. water to which was added 40 cc. concentrated hydrochloric acid. The solution was then diluted with 100 cc. water. The solution so produced was allowed to contact 100 grams of gamma alumina 1/16 inch diameter extrudates for two hours. The excess liquid was then decanted off, and the impregnated extrudates were washed with a solution consisting of 30% concentrated NH₄ OH and 70% water until the extrudates were chloride free. The extrudates were then washed with 500 cc. water and calcined for 2 hours at 932° F. The catalyst contained 10.2% bismuth components (calculated at Bi₂ O₃) supported on gamma alumina.

4.5 weight percent Bi₂ O₃ -9.4 weight percent V₂ O₅ on silica alumina

This catalyst was prepared by first preparing the 10 weight percent V₂ O₅ on silica-alumina catalyst as described above. One hundred grams of this catalyst was contacted with a solution prepared by first dissolving 11.6 gm bismuth nitrate in 100 cc. water to which was added 5 cc. concentrated nitric acid, and then further adding sufficient water to make the solution up to 120 cc. The contacting time was 2 hours, after which the excess liquid was decanted off. The impregnated extrudates were then dried at 230° F. overnight and calcined for 2 hours at 932° F. in the presence of air. The finished catalyst contained 4.5 weight percent bismuth components (calculated as Bi₂ O₃) and 9.4 weight percent vanadium components (calculated as V₂ O₅). By X-ray diffraction analysis, it was determined that the finished catalyst contained bismuth orthovanadate.

7.95 weight percent Bi₂ O₃ -9.0 weight percent V₂ O₅ on silica alumina

This catalyst was prepared according to the method shown above for the 4.5 weight percent Bi₂ 0₃ -9.4 weight percent V₂ O₅ catalyst except that the impregnating solution was prepared as follows: 23.2 gm bismuth nitrate were dissolved in 100 cc. of water plus 10 cc. nitric acid. The solution was then sufficiently diluted with water to provide a total volume of 120 cc. The finished catalyst contained 7.95 weight percent of bismuth components (as Bi₂ O₃) and 9.0 weight percent vanadium components (as V₂ O₅). The catalyst was found by X-ray diffraction analysis to contain bismuth orthovanadate.

11.6 weight percent Bi₂ O₃ -8.63 weight percent V₂ O₅ on silica-alumina

This catalyst was prepared according to the method shown in Example II.

Each of the foregoing catalysts was utilized to incinerate H₂ S to SO₂ under the conditions recited in Example III. The only condition which was varied for the individual catalysts was operating temperature. After operating with the various catalysts for several days duration at temperatures varying between about 450° and 510° F., the stability of each catalyst was determined by comparing the concentration of unreacted H₂ S in a sample of the product gas at a specified operating temperature early in the run versus the concentration of unreacted H₂ S in a sample of the product gas produced at the same specified temperature later in the run. The data so obtained are tabulated in Table II, and the stabilities of the various catalysts, in terms of the increase of unreacted H₂ S in the product gas per day, are also tabulated in Table II. As shown, the catalysts which proved most stable were those consisting of bismuth components or bismuth and vanadium components as the essential active catalytic components. Catalysts containing only vanadium components as the essential active catalytic components deactivated at unacceptably high rates. The most stable catalysts were those containing bismuth and vanadium components in proportions of at least about 8.0 weight percent and 7.0 weight percent, respectively. Such catalysts proved remarkably more stable than the 10% or 36.6% V₂ O₅ catalyst and roughly twice as stable as the 10.2% Bi₂ O₃ catalyst.

Also significant is the fact that the two catalysts containing at least about 8.0 weight percent bismuth components and at least about 7.0 weight percent vanadium components maintained an H₂ S concentration in the product below about 3.5 ppmv in comparison to about 6 ppmv for the vanadium-bismuth catalyst containing only 4.5 weight percent bismuth. Many environmental regulations permit no more than about 10 ppmv of H₂ S to be discharged to the atmosphere, and it can be seen that the two vanadium-bismuth catalysts containing at least about 8.0 weight percent bismuth components provide activity and stability that will insure against reaching such high levels of H₂ S in the product gas whereas the 4.5 weight percent bismuth-9.4 weight percent vanadium catalyst is less suitable for this purpose. Of special note is the high stability of the 11.6 weight percent bismuth-8.63 weight percent vanadium catalyst. Because of the high stability and high activity of this catalyst, it and other catalysts containing at least 10 weight percent bismuth components, calculated as Bi₂ O₃, and at least 8.0 weight percent vanadium components, calculated as V₂ O₅, are most highly preferred in the invention.

                                      TABLE II                                     __________________________________________________________________________                  ppmv H.sub.2 S in                                                                     ppmv H.sub.2 S in   Deactivation                                        Product at                                                                            Product at                                                                            Operating                                                                               t.sub.2 - t.sub.1                                                                  Rate.sup.1,                            Catalyst     Time, t.sub.1                                                                         Time, t.sub.2                                                                         Temperature, °F.                                                                 Days                                                                               ppmv H.sub.2 S/day                     __________________________________________________________________________     10% V.sub.2 O.sub.5                                                                         1.5    46.8   500      7.5 6.04                                   36.6% V.sub.2 O.sub.5                                                                       1.5    51.5   ˜450                                                                              16.9                                                                               2.96                                   10.2% Bi.sub.2 O.sub.3                                                                      3.3    12.2   510      14.1                                                                               0.63                                   4.5% Bi.sub.2 O.sub.3 --9.4% V.sub.2 O.sub.5                                                2.9    6.0    450      9.9 0.31                                   7.95% Bi.sub.2 O.sub.3 --9.0% V.sub.2 O.sub.5                                               1.4    3.5    450      6.0 0.35                                   11.6% Bi.sub.2 O.sub.3 --8.63% V.sub.2 O.sub.5                                              0.5    3.0    450      11.0                                                                               0.23                                   __________________________________________________________________________      .sup.1 Deactivation Rate = (ppmv H.sub.2 S in product at t.sub.2 - ppmv        H.sub.2 S in product at t.sub.1) ÷ (t.sub.2 - t.sub.1) days.         

EXAMPLE V

To compare the intial activities of the catalysts of the invention against vanadia catalysts and bismuth catalysts, data comparing the product H₂ S obtained at various temperatures in the runs of Example IV prior to any significant catalyst deactivation were tabulated in Table III. Also tabulated in Table III are data obtained from an experiment run under the same conditions of Example III but using a catalyst consisting of 13.0 weight percent Bi₂ O₃ and silica-alumina (75% SiO₂ -25% Al₂ O₃), which catalyst was prepared by impregnating silica-alumina extrudates with a bismuth nitrate solution followed by calcination at 932° F. for two hours in the presence of air.

As shown in Table III, the vanadia and vanadium-bismuth catalysts had activities yielding similar results under the conditions of the experiment, i.e., both catalysts left almost no unreacted H₂ S at temperatures in the 420° to 450° F. range. On the other hand, the 10.2% and 13.0% bismuth catalysts were only useful at temperatures above about 500° F. for providing a product nearly free of unreacted H₂ S. At temperatures in the 490° to 500° F. range, the two bismuth catalysts both showed evidence of loss of activity, with unreacted H₂ S being as high as 50 ppmv. Thus, the vanadia and vanadium-bismuth catalysts exhibited substantially better activity for the conversion of H₂ S to SO₂ than the catalysts containing only bismuth components as the essential active catalytic components.

                  TABLE III                                                        ______________________________________                                         Catalyst        Temperature, °F.                                                                     ppmv H.sub.2 S                                    ______________________________________                                         10% V.sub.2 O.sub.5                                                                            445          4.4                                                               490          3.4                                                               500          1.5                                               36.6% V.sub.2 O.sub.5                                                                          400          25                                                                410          17                                                                420          4.8                                                               440          1.5                                               10.2% Bi.sub.2 O.sub.3                                                                         500          50                                                                510          11.8-13.4                                                         520          3.3-8.6                                                           530          3.6                                               13.0% Bi.sub.2 O.sub.3                                                                         490          17.1                                                              500          ˜1.0                                                        510          0.9                                               4.5% Bi.sub.2 O.sub.3 --9.4% V.sub.2 O.sub.5                                                   440-450° F.                                                                          1.7-6.0                                           7.95% Bi.sub.2 O.sub.3 --9.0% V.sub.2 O.sub.5                                                  450-460° F.                                                                          1.1-3.5                                           11.6% Bi.sub.2 O.sub.3 --8.63% V.sub.2 O.sub.5                                                 450-470° F.                                                                          0.3-4.5                                           ______________________________________                                    

Because the data shown in Table III were obtained from a laboratory experiment using only about 15 cc of catalyst in an isothermal reactor vessel, the conditions of operation, and particularly the use of temperatures above 400° F., were not conducive to distinguishing the difference in catalytic activity between vanadia catalysts and vanadium-bismuth catalysts for the oxidation of H₂ S to SO₂. As the data in Table III show, both catalysts under the conditions of the experiment drive the conversion to SO₂ essentially to completion at temperatures above about 420° F., and thus, to distinguish the activities of the two catalysts, a second experiment was performed under adiabatic conditions with much larger volumes of catalyst and at temperatures below 400° F. In this experiment, which is more fully described in the following Example VI, the vanadia and vanadium-bismuth catalysts are seen to have strikingly different catalytic activities for incinerating H₂ S.

EXAMPLE VI

A sample (1865cc) of cylindrical particulates (1/8 inch diameter) of a vanadium-bismuth catalyst consisting essentially of 7.9 weight percent vanadium components, calculated as V₂ O₅, and 9.0 weight percent bismuth components, calculated as Bi₂ O₃, on a support consisting essentially of 75% SiO₂ and 25% Al₂ O₃ was charged to a reactor vessel of pilot plant size. This catalyst, which had a surface area of 330 m² /gm, a pore volume of 0.64 cc/gm, and a compacted bulk density of 0.65 g/cc, had previously been used over a 118-day time period for oxidizing H₂ S in various experiments; the catalyst was, therefore, not fresh catalyst but was subjected to an activation treatment with air at 400° F. prior to the test run now to be described.

A gas stream consisting essentially of 1 volume percent H₂ S, 7 volume percent water vapor, 18.5 volume percent air (providing 2.59 times the oxygen necessary for complete conversion to SO₂) and the balance being CO₂ was passed through the reactor vessel at a gas hourly space velocity of 2,000 v/v/hr and an inlet pressure between about 25 to 30 p.s.i.a. and an outlet pressure between about 15 and 20 p.s.i.a. The reactor was operated under simulated adiabatic conditions, that is, the only heat introduced to the reactor vessel was that which would make up for losses due to inadequate insulation and the like.

Operating in the foregoing manner, and at 340° F. inlet temperature, essentially complete conversion of H₂ S to SO₂ was obtained, as determined by the absence of sulfur formation in the piping conduits carrying the product gases. Had substantial H₂ S been present, elemental sulfur would have formed by the reaction of product SO₂ with unreacted H₂ S and deposited by condensation in the product piping conduits.

The reactor vessel was subsequently charged with 1865 cc. of 1/8 inch diameter particles of vanadia catalyst consisting essentially of 9.12 weight percent vanadium components, calculated as V₂ O₅, on a silica-alumina (25% alumina) support, said catalyst having a surface area of 340 m² /gm and a compacted bulk density of 0.53 gm/cc. This catalyst had only been in use for five days for various H₂ S oxidation experiments, and thus was essentially fresh catalyst. But to be certain that the catalyst was in a fully oxidized form, it was activated using air at 700° F.

The vanadia catalyst was used under the same operating pressure and gas hourly space velocity conditions as for the vanadium-bismuth catalyst, but the composition of the gas stream contained substantially more oxygen. More specifically, the composition of the gas stream was as follows: 1 volume percent H₂ S, 7 volume percent water vapor, 48 volume percent air (providing 6.72 times the amount of oxygen for full reaction to SO₂, compared to only 2.59 times the necessary amount in the run using the vanadium-bismuth catalyst), and the balance CO₂.

Due to the greater proportion of oxygen in the feed gas of the second run compared to the first, the conditions for producing SO₂ with the vanadia catalyst were far more favorable than were those used with the vanadium-bismuth catalyst. But despite this decided advantage, the vanadia catalyst proved far less active for incinerating H₂ S. Essentially complete conversion to SO₂, as determined by the absence of sulfur formation in the product piping conduits, could not be achieved at inlet temperatures throughout the 370° to 400° F. range. These inlet temperature conditions consistently yielded large sulfur deposits in the product piping under simulated adiabatic conditions. Only with non-adiabatic conditions, when heat above that required for adiabatic conditions was added to the reactor vessel, could the conversion to SO₂ be maintained without sulfur deposition at inlet temperatures of 370° to 400° F.

From the results of the foregoing comparative experiment, it was concluded that the vanadium-bismuth catalyst was a more active catalyst than the vanadia catalyst for incinerating H₂ S by virtue of the fact that essentially complete conversion was obtained at an inlet temperature of only 340° F. whereas the vanadia catalyst, under more favorable oxygen conditions, could not drive the conversion to completion at the higher temperatures of 370° to 400° F. The catalyst of the invention, therefore was determined to be substantially more active than the vanadia catalyst for oxidizing H₂ S to SO₂.

The catalyst of the invention may also be utilized to oxidize H₂ S to elemental sulfur as well as to SO₂. To produce elemental sulfur, conditions are usually chosen for adiabatic or isothermal reactors from the following ranges: 250° to 900° F., 100 to 10,000 v/v/hr, and 5 to 75 p.s.i.a. Typical space velocity and pressure conditions fall in the ranges of 100 to 10,000 v/v/hr and 5 to 75 p.s.i.a., respectively, with space velocities of 500 to 1500 v/v/hr and pressures of 15 to 20 p.s.i.a. being among the conditions most often employed. Operating temperature is of importance in the process, for the conversion to sulfur in the gas phase is dramatically affected by temperature, the sulfur yield increasing with decreasing temperature below about 1000° F. On the other hand, if the operating temperature drops below the sulfur vapor dew point, then sulfur may condense on the catalyst, which, although easily removable by raising the temperature, is an inconvenience usually to be avoided. Taking the foregoing into consideration, the temperatures chosen for operation to maximize the yield to sulfur are below about 475° F., especially below about 450° F., while temperatures below about 250° F., although contemplated as operative with the preferred catalyst of the invention, are generally avoided due to increasing problems with sulfur condensation. Sulfur begins to condense at about 260° F. under atmospheric pressure, and to operate without sulfur deposition under pressure conditions around atmospheric, the temperature must be maintained above 260° F., as for example, by maintaining the temperature of reaction at or above 275° F.

Because of the high activity of the catalyst of the invention, relatively low temperatures of initiation may be employed, which, in addition to aiding in maximizing the yield of sulfur, also reduces the amount of preheating required to treat relatively low temperature H₂ S-containing feed gases, thereby saving on energy costs. Of course, the minimum temperature at which ignition will commence varies according to the nature of the feed gas, the catalyst selected, the space velocity, and other factors, but in the usual instance, a temperature of initiation at least below 400° F. is employed, with progressively lower temperatures, as for example below 350° F., below 325° F., below 300° F., and down to the usual minimum temperature of operation under atmospheric pressure conditions, i.e., 275° F., progressively taking greater and greater advantage of the superior activity and other properties of the catalyst of the invention.

The conversion of H₂ S to sulfur also requires an oxidant gas, and one suitable oxidant gas, oxygen, usually supplied in the form of air, is blended with the feed gas stream containing the H₂ S so as to produce sulfur vapor according to the following reaction:

    2H.sub.2 S+O.sub.2 →3S+2H.sub.2 O                   (II)

Most preferably, the amount of air or oxygen so blended with the feed gas is such that oxygen is present in a proportion near or at the stoichiometric proportion for Reaction (II), usually between about 0.9 and 1.1 times the stoichiometric proportion. As is well known, the highest possible conversions of H₂ S to sulfur are accomplished when oxygen is available in its stoichiometric proportion. Also contributing to high sulfur yields are low water vapor partial pressures and, as stated hereinbefore, relatively low operating temperatures.

It is, of course, well known that SO₂ may be used in place of oxygen for the conversion of H₂ S to sulfur, the sulfur being formed by the following reaction:

    2H.sub.2 S+SO.sub.2 →3S+2H.sub.2 O                  (III)

Thus, if SO₂ is present in the feed gas stream in any H₂ S to SO₂ ratio greater than 2.0, oxygen need only be added in an amount sufficient to react with the H₂ S not converted by Reaction (III). In other words, if the ratio of H₂ S to SO₂ is greater than 2.0, then the stoichiometric proportion of oxygen is that proportion sufficient to provide a molar or volumetric ratio of H₂ S to (SO₂ +O₂) equal to 2.0.

For feed gases inherently containing H₂ S and SO₂ in an H₂ S-to-SO₂ ratio less than 2.0, the highest possible conversions to sulfur are obtained by firstly pretreating the feed so as to convert the SO₂ to H₂ S, as by the method shown hereinbefore in U.S. Pat. No. 3,752,877, and then blending the pretreated gas with sufficient oxygen or air to provide an H₂ S to O₂ ratio equal to 2.0. For feed gases containing H₂ S to SO₂ in a ratio equal to 2.0, no pretreatment or addition of oxygen is necessary; the catalyst may be used for the direct conversion of H₂ S to sulfur via Reaction (III).

In view of the foregoing, it should be apparent that, when elemental sulfur is desired, SO₂ may be utilized as an alternative oxidant to oxygen. That is, for any gas stream containing H₂ S, elemental sulfur may be produced herein by blending either SO₂ or oxygen oxidant with the gas stream such that a ratio of H₂ S to oxidant of 2.0 is provided. However, oxygen is inherently superior to SO₂, not only because of its ready availability in the form of air but also due to the higher conversions to sulfur obtainable therewith. A comparison of Reactions (II) and (III) reveals that, for the same amount of H₂ S converted to sulfur, 50% more sulfur is formed by Reaction (III) with SO₂ oxidant than by Reaction (II) with O₂ oxidant. The formation of 50% more sulfur by Reaction (III) necessitates higher operating temperatures for Reaction (III) than for Reaction (II) if the sulfur vapor dew point is not to be exceeded. But at operating temperatures below 1000° F., the conversion of H₂ S to sulfur decreases with increasing temperature. Thus, because H₂ S can be converted to sulfur by Reaction (II) at a lower temperature than Reaction (III) without exceeding the dew point, an inherent advantage--i.e., a higher conversion--is obtained when oxygen is used as oxidant than when SO₂ is utilized.

Whether oxygen or SO₂ is utilized as oxidant, it will be found that the catalyst of the invention is highly useful for converting H₂ S to element sulfur. The percentage conversion in any given situation, of course, will depend upon such factors as operating temperature, operating pressure, water vapor partial pressure, and choice of oxidant. But the vanadium-bismuth catalysts disclosed hereinbefore usually provided a conversion of H₂ S to elemental sulfur within 10%, often within 5%, of theoretical. And because of their high activity for converting H₂ S to sulfur, the vanadium-bismuth catalyst of the invention provides high conversions of H₂ S to sulfur under lower operating temperature and/or higher space velocity conditions than are required for typical vanadia catalysts, disclosed, for example, in U.S. Pat. No. 4,243,647.

The following Example demonstrates the high activity of vanadium-bismuth catalysts for oxidizing H₂ S to elemental sulfur.

EXAMPLE VII

A catalyst was prepared containing 8.7 weight percent vanadium components, calculated as V₂ O₅, and 12.9 weight percent bismuth components, calculated as Bi₂ O₃, and the balance being a support consisting of silica-alumina having a 25% by weight alumina content. The catalyst was in particulate form, had a surface area of 239 m² /gm, and a compact bulk density of 0.67 g/cc. (This catalyst was prepared in a manner very similar to that described in Example II.)

The foregoing catalyst (950 gm) was charged to an isothermal reactor and utilized to treat a feed gas containing (on an anhydrous basis) about 99% CO₂ and H₂ S in a concentration varying between about 750 ppmv and 1200 ppmv. Air was blended with the feed gas such that stoichiometric oxygen was available within a 10% tolerance to oxidize the H₂ S in the feed gas to sulfur. Elemental sulfur produced in the reactor was removed therefrom in the vapor form and recovered by condensation. The experiment was conducted over a time period of more than five months, and the data shown in Table IV were derived from analyses of samples of the feed and product gases when the operating conditions were those shown in Table IV.

It is noted with respect to the foregoing experiment that the catalyst throughout the run evinced no deactivation, except when the operating temperature fell below the sulfur vapor dew point temperature and sulfur deposited on the catalyst. Such deactivations, however, were only temporary, elevated temperatures restoring the catalyst to full activity.

                                      TABLE IV                                     __________________________________________________________________________     Sample No.     809  1232 1520 1544                                                                               1568 1716                                                                               1764 2130 2150 2322                 __________________________________________________________________________     Water Vapor Pressure, psia                                                                    3    3    3    3   3    5   5    5    2.5  5.0                  Operating Pressure, psia                                                                      300  300  300  300 300  300 300  300  150  300                  Operating Temperature, °F.                                                             381  334  305  295 285  310 300  410  410  410                  Feed H.sub.2 S, ppmv                                                                          1050 1050 852  875 875  780 890  1132 1032 1137                 Product H.sub.2 S, ppmv                                                                       68   48   44   29  84   111 120  143  213  162                  Product SO.sub.2, ppmv                                                                        88   45   47   73  25   40  62   65   64   86                   Sulfur Yield, %                                                                               77.7 83.8 82.3 81.3                                                                               77.4 75.4                                                                               75.7 77.0 70.4 68.7                 GHSV (at 60° F. and 1 atm)                                                             750  750  750  750 750  750 750  750  750  975                  __________________________________________________________________________

One surprising aspect of the invention evidenced by the data in Table IV is the high stability of the vanadium-bismuth catalyst in the presence of water vapor. As shown previously by the data in Table II, vanadia catalysts deactivate rapidly in the presence of water vapor at temperatures below about 600° F., but the data in Table IV show that vanadium-bismuth catalysts resist such deactivation, even when utilized in the presence of water vapor at a partial pressure of 2.5 to 5.0 p.s.i.a. for a time period greater than five months.

Another surprising aspect of the invention revealed by the data in Table IV is that the vanadium-bismuth catalyst is active for lighting off the conversion of H₂ S to sulfur at temperatures well below 300° F. This result is considered surprising for a number of reasons, not the least of which is that vanadia catalysts, which are known to be highly active for converting H₂ S to elemental sulfur, are nevertheless less active than vanadium-bismuth catalysts for lighting off the oxidation of H₂ S to sulfur. As will now be shown in the following Example VIII, vanadium-bismuth catalysts are far more active for oxidizing H₂ S to elemental sulfur and initiate the oxidation of H₂ S to sulfur at a much lower temperature than is the case for a vanadia catalyst treating the same feed gas-oxidant blend.

EXAMPLE VIII

In this Example, an experiment is described wherein the light-off characteristics of a vanadium-bismuth catalyst and a vanadia catalyst are compared for the oxidation of H₂ S to sulfur.

Two catalysts were prepared, both with supports consisting essentially of silica-alumina (75% SiO₂ and 25% Al₂ O₃). The first catalyst, the vanadia catalyst, contained 16.4 weight percent vanadium components, calculated as V₂ O₅, while the second contained 9.7 weight percent vanadium components, calculated as V₂ O₅, and 11.2 weight percent bismuth components, calculated as Bi₂ O₃. Both catalysts were prepared in an air-calcined form.

The catalysts were placed into separate but essentially identical reactor vessels and then tested simultaneously in a parallel operational mode to determine, with an identical feed gas treated under essentially identical conditions of pressure and weight hourly space velocity, the difference between the two catalysts with respect to kindling the reaction of H₂ S to sulfur using oxygen oxidant. The feed gas-oxidant blend was produced by mixing H₂ S at a rate of 39.60 scc/min with air flowing at 94.23 scc/min and nitrogen at 1845.82 scc/min, thereby providing a feed gas-oxidant gas stream flowing at a rate of 1979.70 scc/min and consisting essentially of 2.0 mole percent H₂ S, 1.0 mole percent free oxygen, and about 97.0 mole percent nitrogen. Through use of independent control valves, the flow rate of the gas stream into each reactor vessel was maintained as closely as possible to identical rates of about 989.85 scc/min, and the operating pressure maintained in both reactor vessels was about 14.7 p.s.i.a.

The catalysts were employed in the experiment in identical amounts on a weight basis, i.e., 1.50 grams, although, due to density differences, the volumetric amount of the vanadium-bismuth catalyst employed was only 2.0 cc. in comparison to 3.0 cc. for the vanadia catalyst. Thus, both catalysts were employed under essentially identical space velocity conditions as determined by catalyst weight, i.e., 39,515 volumes of gas (in cubic centimeters) per gram of catalyst per hour, but on a volumetric basis, the gas hourly rate for the vanadium-bismuth catalyst was 1.5 times greater than that of the vanadia catalyst. More specifically, the volumetric space velocity for the vanadia catalyst was only about 19.797 v/v/hr as compared to 29,695.5 v/v/hr for the vanadium-bismuth catalyst.

The two reactor vessels were initially maintained at an operating temperature of about 265° F., in large part because a lower temperature would result in sulfur deposition and possible pluggage of the operating equipment. The product gas streams were then analyzed to determine if either catalyst exhibited activity for oxidizing H₂ S at 265° F. under the conditions specified above, which conditions included an H₂ S to O₂ ratio in the feed gas-oxidant blend maintained at the stoichiometric value for the conversion to sulfur. However, due to the analytical difficulty involved in measuring sulfur vapor in a gas stream, and because some SO₂ would concomitantly form under light-off conditions also producing sulfur, the product gas was analyzed for the presence of SO₂. At the initial operating temperature of 265° F., no SO₂ was detected in the product gas recovered from the reactor containing the vanadia catalyst, but that from the reactor containing the vanadium-bismuth catalyst yielded 536 ppmv of SO₂. It was thus determined that, under the conditions of the experiment, the light-off temperature for the vanadium-bismuth catalyst was below about 265° F. As to the vanadia catalyst, incremental increases in the operating temperature eventually resulted in a 2 to 3 ppmv breakthrough of SO₂ at 318° F., with 473 ppmv being produced at 370° F. and 609 ppmv being produced at 390° F.

The results of the experiment establish that the vanadium-bismuth catalyst of the invention ignites the reaction of H₂ S to sulfur at a lower temperature than that for the vanadia catalyst, the vanadia catalyst initiating no reaction whatever until the operating temperature was 53° F. higher than the 265° F. temperature at which the vanadium-bismuth catalyst proved highly active. And based on the data obtained at 265°, 370°, and 390° F., the vanadia catalyst required an operating temperature some 105° to 125° F. greater than that for the vanadium-bismuth catalyst to provide a comparable product.

The results of the experiment are all the more indicative of the superiority of the vanadium-bismuth catalyst when it is taken into account that the procedure of the experiment was, if anything, more favorable to the vanadia catalyst. In this regard, it is noted that, by volume, 50% more vanadia catalyst was utilized, so that the volumetric space velocity for the vanadia catalyst was only two-thirds of that for the vanadium-bismuth catalyst. In addition, although the vanadium-bismuth catalyst had somewhat more metals thereon by weight, the vanadium-bismuth catalyst, due to the relatively high atomic weight of bismuth, actually had less total atoms of active metals thereon. More specifically, the vanadia catalyst contained 1.80 millimoles of vanadium (as the metal) per gram of catalyst whereas the vanadium-bismuth catalyst contained only 1.55 millimoles of total vanadium and bismuth (as the metals) per gram; yet the vanadium-bismuth catalyst proved highly superior to the vanadia catalyst.

In a specific embodiment of the invention particularly useful for treating feed gas streams containing between about 5 and 40 volume percent H₂ S, especially when the feed gas stream contains water vapor at relatively high partial pressures, e.g., above about 2.0 p.s.i.a. and, more usually, above about 4.0 p.s.i.a., the feed gas stream is blended with air, preferably in a stoichiometric amount, and the resulting blended gases are passed through an adiabatic reactor containing a particulate vanadium-bismuth catalyst under conditions described hereinbefore such that a substantial proportion of the H₂ S is converted to elemental sulfur vapor. The product gas containing elemental sulfur is passed to a sulfur condenser or other suitable means for separating sulfur from the product gas, leaving a purified product gas containing residual H₂ S. A portion of the purified product gas is then recycled and blended with the feed gas such that the blend of feed gas, air, and recycle gas entering the reactor contains H₂ S in a predetermined range, such as 3 to 6 volume percent, or below a predetermined maximum, typically and preferably, 5 volume percent. The remaining portion of the purified product gas is treated by any of three methods. The three methods (which are applicable to any embodiment of the invention in which the H₂ S content of a gas stream recovered after treatment with the vanadium-bismuth catalyst is too high for discharge to the atmosphere) are:

(1) If the H₂ S to SO₂ volumetric ratio in the purified product gas stream is about 2.0, this gas stream may be contacted with any porous refractory oxide-containing catalyst, such as alumina, under conditions of elevated temperature, e.g., 400° to 900° F., such that a substantial proportion of the H₂ S is converted by Reaction (III) to elemental sulfur, which is then recovered, as by condensation. In this embodiment of the invention, it will usually be found that an alumina catalyst will provide sufficient activity for oxidizing the H₂ S in the purified product gas stream to sulfur. But if higher activity is desired, vanadia catalysts, such as those described in U.S. Pat. No. 4,243,647, may be employed, as may vanadium-bismuth catalysts of the present invention if yet higher activity is desired. One advantage of a catalyst of increased activity is that the same conversion of H₂ S may be accomplished but under less favorable operating conditions, as for example, a lower operating temperature or a higher space velocity.

(2) If the H₂ S to SO₂ volumetric ratio of the purified product gas is substantially above 2.0, or if one desires to allow for fluctuations in the H₂ S to SO₂ ratio, then the purified product gas is treated in accordance with another embodiment of the invention by blending sufficient air to provide a volumetric ratio of H₂ S/(SO₂ +O₂) of about 2.0 and contacting the resulting mixed gases with a vanadium-bismuth catalyst under conditions hereinbefore disclosed for conversion to elemental sulfur. In this embodiment of the invention, an alumina catalyst would not be a suitable choice for an alternative or substitute catalyst to vanadium-bismuth catalysts, the reaction of H₂ S with oxygen to produce sulfur not being readily promoted by alumina catalysts. However, a vanadia catalyst, for example, a catalyst consisting essentially of one or more vanadium oxides or sulfides on a porous refractory oxide support, may be substituted to treat the purified product gas, provided one is willing to tolerate lower catalytic activity. The lower activity may be considered acceptable in certain instances, as for example, if the cost of the catalyst is of special importance. But if the vanadia catalyst is utilized, not only will lower activity result, but the catalyst becomes subject to deactivation when the water vapor partial pressure is more than about 1.0 p.s.i.a. and the operating temperature is below about 600° F., the deactivation rate increasing with increasing water vapor partial pressures above 1.0 p.s.i.a.

(3) If the H₂ S content of either the purified product gas stream or the gas streams recovered after sulfur condensation from methods (1) and (2) above is too high for discharge to the atmosphere, but such gas streams could be discharged to the atmosphere if the H₂ S were converted to SO₂ (due to less stringent air pollution standards for SO₂ than for H₂ S), such gas streams are subjected to incineration to convert the H₂ S therein to SO₂. The incineration may be accomplished thermally at temperatures above about 1000° F. in the presence of excess oxygen, but it is preferred that the incineration be accomplished catalytically by contact with the vanadium-bismuth catalyst of the invention as described hereinbefore under the range of conditions for conversion to SO₂ as also described hereinbefore. Use of the vanadium-bismuth catalyst provides a distinct advantage over thermal incineration in that the gas stream to be treated does not require as much preheating, the vanadium-bismuth catalyst being active for the conversion of H₂ S to SO₂ at temperatures substantially below 500° F. For example, it has been found that the vanadium-bismuth catalyst described in Example VI is effective for oxidizing H₂ S to SO₂ using excess oxygen at temperatures of 300° to 310° F., and the data obtained in the experiment of Example VIII, although conducted under partial oxidizing conditions for the production of elemental sulfur, indicate that yet lower temperatures, at or below 265° F., initiate conversion to SO₂.

Treating H₂ S-containing feed gas streams in accordance with one or more of the foregoing embodiments proves highly effective for removing H₂ S and recovering sulfur. As an illustration, in one embodiment of the invention, a gas stream containing about 13 volume percent H₂ S is diluted with recycle gas so as to reduce the H₂ S concentration to 5 volume percent, and the resultant blend is then passed serially through four catalyst chambers, the first containing vanadium and bismuth components supported on silica-alumina, the second and third containing alumina catalysts, and the final one containing another catalyst of vanadium and bismuth on silica-alumina. In the first chamber, the H₂ S is oxidized with added air to elemental sulfur, which is separated by condensation from a purified product gas stream. In the second and third chambers, unreacted H₂ S and SO₂ produced in the first chamber react to produce yet more sulfur, the sulfur being removed from the effluents of each chamber by condensation. Passage of remaining gases through the final catalyst chamber under incineration conditions converts residual H₂ S to SO₂, and, overall, over 95%, usually about 97%, of the sulfur carried with the feed gas in the form of H₂ S is recovered as elemental sulfur, and less than about 5% is discharged from the incinerator to the atmosphere in the form of SO₂.

Although the invention has been described in conjunction with specific examples and embodiments thereof, it is evident that many alterations, modifications, and variations will be apparent to those skilled in the art in light of the foregoing description. For example, it should be self-evident that the catalytic process of the invention may easily be modified to oxidize H₂ S to any desired percentage combination of sulfur and SO₂ by simply controlling the proportion of oxygen between the amount required for Reaction (I) and that required for Reaction (II). Accordingly, it is intended in the invention to embrace these and all such alternatives, modifications, and variations as may fall within the spirit and scope of the appended claims. 

We claim:
 1. In a process for oxidizing H₂ S to elemental sulfur in the gas phase by contact of H₂ S with a catalyst in the presence of oxygen or SO₂ at an elevated temperature, the improvement wherein said catalyst comprises vanadium and bismuth components and said oxidizing results in a substantial conversion to sulfur, with at least some conversion to sulfur taking place at a temperature below about 475° F.
 2. A process as defined in claim 1 wherein oxygen is present during said contact of H₂ S and said catalyst.
 3. A process as defined in claim 2 wherein said catalyst is also in contact with one or more components selected from the group consisting of H₂, CO, NH₃, and light hydrocarbons, but essentially none of said components is oxidized during said contact.
 4. A process as defined in claim 1 wherein said catalyst comprises vanadium components selected from the group consisting of vanadium oxides and sulfides and bismuth components selected from the group consisting of bismuth oxides and sulfides.
 5. A process as defined in claim 4 wherein said catalyst consists essentially of at least 8 weight percent vanadium components, calculated as V₂ O₅, and at least 10 weight percent bismuth components, calculated as Bi₂ O₃, on a porous refractory oxide support consisting essentially of silica-alumina containing between about 20 and 30 weight percent alumina.
 6. A process as defined in claim 1 or 4 wherein said H₂ S is initially present during said contact in a proportion between about 500 ppmv and 10.0 volume percent.
 7. A process as defined in claim 1 or 4 wherein oxygen is present in a proportion between about 0.9 and 1.1 times the stoichiometric proportion necessary for the conversion of said H₂ S to sulfur.
 8. A process as defined in claim 7 wherein said oxidizing is initiated at a temperature between about 250° and about 325° F.
 9. A process as defined in claim 1 wherein said catalyst is porous and has a mean pore diameter of at least 50 angstroms.
 10. In a process for oxidizing H₂ S to elemental sulfur in the gas phase by contacting H₂ S with a catalyst in the presence of oxygen or SO₂ at an elevated temperature, the improvement wherein said catalyst comprises vanadium and bismuth components and said contacting takes place in the presence of water vapor at a partial pressure more than about 1.0 p.s.i.a., with said oxidizing resulting in a substantial conversion to sulfur, and with said oxidizing being initiated at a temperature below about 475° F.
 11. A process as defined in claim 10 wherein water vapor is present at a partial pressure of at least 1.5 p.s.i.a.
 12. A process as defined in claim 10 wherein water vapor is present at a partial pressure between about 1.5 and 10.0 p.s.i.a.
 13. A process as defined in claim 10 wherein water vapor is present at a partial pressure of at least 2.0 p.s.i.a.
 14. A process as defined in claim 10 wherein water vapor is present at a partial pressure of at least about 4.0 p.s.i.a.
 15. A process as defined in claim 13 or 14 wherein said catalyst comprises vanadium components selected from the group consisting of vanadium oxides and sulfides and bismuth components selected from the group consisting of bismuth oxides and sulfides on a porous refractory oxide support.
 16. A process as defined in claim 15 wherein oxygen is present during said contact of H₂ S and said catalyst.
 17. A process as defined in claim 16 wherein said oxidizing is initiated at a temperature between about 250° and about 325° F.
 18. A process as defined in claim 17 wherein said water vapor partial pressure is above about 75% of the saturation pressure and the mean pore diameter of the catalyst is 200 angstroms or more.
 19. A process for oxidizing H₂ S in the gas phase comprising (1) contacting H₂ S and free oxygen with a solid catalyst comprising catalytically active vanadium and bismuth components on a carrier material in a reaction zone under conditions such that H₂ S reacts with free oxygen in said reaction zone to effect a substantial conversion of said H₂ S to elemental sulfur, with at least some conversion to elemental sulfur taking place in said reaction zone at a temperature below about 475° F. and (2) removing elemental sulfur from said reaction zone.
 20. A process as defined in claim 19 wherein said oxygen is supplied in the form of air.
 21. A process as defined in claim 20 wherein elemental sulfur vapor removed from said reaction zone is recovered by condensation.
 22. A process as defined in claim 20 wherein said reaction zone is maintained between about 275° and about 425° F. and said catalyst is in particulate form.
 23. A process as defined in claim 22 wherein said catalyst comprises vanadium oxides or sulfides and bismuth oxides or sulfides on a refractory oxide support.
 24. A process as defined in claim 23 wherein said catalyst contains more than about 7 weight percent vanadium components, calculated as V₂ O₅, and more than about 8 weight percent bismuth components, calculated as Bi₂ O₃.
 25. A process as defined in claim 24 wherein said catalyst support is silica-alumina having an alumina content between about 20 and 30 weight percent.
 26. A process as defined in claim 19 wherein the initial contacting in said reaction zone is at a temperature below about 350° F., with at least some of said H₂ S reacting with said oxygen to produce elemental sulfur at temperatures below 350° F.
 27. A process as defined in claim 26 wherein that portion of said reaction zone which is at a temperature below about 350° F. contains water vapor in contact with said catalyst at a water vapor partial pressure above about 2.0 p.s.i.a. with the total pressure being between about 5 and 300 p.s.i.a.
 28. A process as defined in claim 26 or 27 wherein said free oxygen is present in a proportion between about 0.9 and 1.1 times the stoichiometric proportion necessary for conversion of said H₂ S to sulfur.
 29. A process as defined in claim 19 wherein water vapor is present in said reaction zone at a partial pressure of at least 1.5 p.s.i.a.
 30. A process for the oxidation of H₂ S to elemental sulfur comprising (1) blending a feed gas stream containing H₂ S with air; (2) passing the resulting blend through a reaction zone containing a solid catalyst consisting essentially of catalytically active vanadium and bismuth components on a refractory oxide support under conditions such that H₂ S reacts with the oxygen supplied with said air to produce elemental sulfur vapor, said reaction being initiated at a temperature between about 250° and about 475° F. and resulting in a conversion of at least 68.7 percent of said H₂ S to elemental sulfur; and (3) withdrawing a product gas from said reaction zone containing elemental sulfur vapor produced in said reaction zone.
 31. A process as defined in claim 30 wherein the catalyst is in particulate form and contains vanadium and bismuth components selected from the group consisting of the vanadium oxides and sulfides, the bismuth oxides and sulfides, and the bismuth vanadates.
 32. A process as defined in claim 31 wherein said reaction is initiated at a temperature below about 400° F.
 33. A process as defined in claim 32 wherein said blend contains water vapor at a partial pressure of at least about 4.0 p.s.i.a. and the total pressure in said reaction zone in step (2) is between about 5 and 300 p.s.i.a.
 34. A process as defined in claim 31 or 33 wherein said catalyst consists essentially of at least about 8 weight percent vanadium components, calculated as V₂ O₅, and at least 10 weight percent bismuth components, calculated as Bi₂ O₃, on a porous refractory oxide support.
 35. A process as defined in claim 30 wherein said feed gas stream contains between 500 ppmv and 10 volume percent H₂ S.
 36. A process as defined in claim 35 wherein the amount of air blended with said feed gas is such that the blend in step (2) contains oxygen in essentially the stoichiometric proportion necessary for the conversion of said H₂ S to elemental sulfur vapor.
 37. A process as defined in claim 35 wherein said reaction is initiated at a temperature below about 350° F.
 38. A process as defined in claim 37 wherein oxygen is present in said blend in a proportion between about 0.9 and 1.1 times the stoichiometric proportion necessary for the conversion of H₂ S to sulfur.
 39. A process as defined in claim 30 wherein said reaction is initiated at a temperature below about 300° F.
 40. A process as defined in claim 39 wherein said catalyst contains an X-ray detectable proportion of bismuth vanadates.
 41. A process as defined in claim 39 wherein said catalyst contains more than about 5 weight percent of vanadium components, calculated as V₂ O₅, and more than about 5 weight percent bismuth components, calculated as Bi₂ O₃.
 42. A process as defined in claim 39 wherein said blend contains water vapor at a partial pressure greater than about 2.0 p.s.i.a. while the total pressure in said reaction zone in step (2) is between about 5 and 75 p.s.i.a.
 43. A process as defined in claim 37 or 39 wherein said catalyst comprises vanadium and bismuth components selected from the group consisting of the vanadium oxides and sulfides and the bismuth oxides and sulfides.
 44. A process as defined in claim 43 wherein oxygen is present in said blend in essentially the stoichiometric proportion necessary for conversion of said H₂ S to sulfur.
 45. A process as defined in claim 43 wherein said blend contains water vapor at a partial pressure above about 1.5 p.s.i.a., and wherein the total pressure in said reaction zone is between about 5 and about 300 p.s.i.a., and wherein said catalyst, over a time period of 90 days of passage through said reaction zone, experiences essentially no deactivation.
 46. A process as defined in claim 43 wherein said blend contains water vapor at a partial pressure greater than about 4.0 p.s.i.a., and wherein the total pressure in said reaction zone in step (2) is between 5 and 500 p.s.i.a., and wherein said catalyst, over a time period of 90 days of passage through said reaction zone, experiences essentially no deactivation.
 47. A process as defined in claim 30 wherein said feed gas contains H₂ or NH₃, which remain essentially completely unoxidized in step (2) and are recovered as components of said product gas.
 48. A process as defined in claim 30 wherein said feed gas stream contains between about 0.1 and about 5 volume percent H₂ S.
 49. A process for treating a feed gas stream containing one or more sulfur components selected from the group consisting of SO₂, COS, CS₂, and light mercaptans comprising:(1) simultaneously converting essentially all of said sulfur components to H₂ S by contacting said feed gas stream in a first reaction zone maintained at elevated temperatures between about 300° and 1200° F. with a catalyst comprising one or more active catalytic components selected from the group consisting of nickel, cobalt, iron, tungsten, and molybdenum in the presence of hydrogen and water vapor; (2) contacting the H₂ S-containing gas stream obtained from step (1) in a second reaction zone in the presence of an oxidant gas selected from the group consisting of oxygen and SO₂ with a catalyst comprising catalytically active vanadium and bismuth components on a refractory oxide support under conditions such that a substantial proportion of said H₂ S is converted to elemental sulfur vapor by reaction with said oxidant gas, with at least some of said elemental sulfur being produced at a temperature maintained in said second reaction zone between about 250° and about 475° F.; and (3) separating elemental sulfur from the gas stream produced in step (2).
 50. A process as defined in claim 49 wherein said oxidant gas is oxygen supplied in the form of air, and wherein said catalyst in said step (2) consists essentially of vanadium and bismuth components on a refractory oxide support, with at least some of said vanadium components being in the form of a vanadium oxide or sulfide and at least some of said bismuth components being in the form of a bismuth oxide or sulfide.
 51. A process as defined in claim 50 wherein said oxygen is supplied in step (2) so as to be present in a proportion between about 0.9 and 1.1 times the stoichiometric proportion necessary for the conversion of said H₂ S to sulfur, and wherein the initial contacting in the second reaction zone is at a temperature below about 400° F., with at least some of said H₂ S reacting with said oxygen to produce elemental sulfur at temperatures below 400° F.
 52. A process as defined in claim 51 wherein said contacting in the first reaction zone is at a temperature below about 900° F. and said catalyst in said step (1) comprises cobalt and molybdenum components.
 53. A process as defined in claim 52 wherein the second reaction zone is maintained between about 250° and 450° F.
 54. A process for treating a feed gas stream containing a substantial proportion of H₂ S comprising:(1) blending said feed gas stream with air; (2) contacting the resulting blended gas stream in a reaction zone with a catalyst comprising catalytically active vanadium and bismuth components, said contacting being such that a substantial proportion of the H₂ S in said blended gas stream is converted to elemental sulfur vapor, with at least some elemental sulfur vapor being produced at a temperature maintained in said reaction zone between about 250° and about 475° F.; (3) recovering a product gas stream from step (2) and separating elemental sulfur therefrom, thereby producing a purified product gas stream; and (4) recycling a portion of the purified product gas stream to step (1).
 55. A process as defined in claim 54 wherein said feed gas stream contains between about 5 and 40 volume percent H₂ S and said portion of said purified product gas stream recycled to step (1) is sufficient to produce an H₂ S concentration in said blended gas stream no greater than 5 volume percent.
 56. A process as defined in claim 54 wherein the H₂ S concentration of said feed gas stream is between 5 and 40 volume percent.
 57. A process as defined in claim 55 or 56 wherein said air is blended with said feed gas such that said blended gas stream contains oxygen in a proportion between about 0.9 and 1.1 times the stoichiometric proportion necessary to convert said H₂ S to sulfur.
 58. A process as defined in claim 54 or 56 wherein the initial contacting in said reaction zone is below about 350° F. and at least some reaction of said H₂ S with oxygen to produce sulfur takes place below 350° F.
 59. A process as defined in claim 58 wherein said catalyst comprises a vanadium oxide or sulfide and a bismuth oxide or sulfide.
 60. A process as defined in claim 58 wherein said catalyst consists essentially of vanadium and bismuth components on a refractory oxide support, with said vanadium components comprising a vanadium oxide or sulfide and said bismuth components comprising a bismuth oxide or sulfide.
 61. A process as defined in claim 60 wherein said blended gas stream contains water vapor at a partial pressure above about 1.5 p.s.i.a.
 62. A process as defined in claim 59 wherein said blended gas stream contains water vapor at a partial pressure greater than about 2.0 p.s.i.a.
 63. A process as defined in claim 54 wherein said feed gas stream contains more than 10 volume percent H₂ S and said portion of said purified product gas stream recycled to step (1).
 64. A process as defined in claim 63 wherein said blended gas stream contacted with said catalyst in step (2) contains H₂ S in a concentration in the range of 3 to 6 volume percent.
 65. A process as defined in claim 63 wherein the H₂ S concentration of said blended gas stream in step (2) is maintained at a value within the range of about 3 to 6 volume percent, and wherein the initial contacting in said reaction zone is below about 400° F. and at least some reaction of said H₂ S with oxygen to produce sulfur takes place below 400° F.
 66. A process for treating a feed gas stream containing H₂ S comprising:(1) blending said feed gas stream with air; (2) contacting the resulting blended gas stream in a first reaction zone with a catalyst consisting essentially of vanadium and bismuth components on a refractory oxide support, said vanadium components comprising a vanadium oxide or sulfide and said bismuth components comprising a bismuth oxide or sulfide, and said contacting being such that a substantial proportion of the H₂ S in the blended gas stream is converted to elemental sulfur vapor by reaction with oxygen but some residual H₂ S remains, with at least some of said elemental sulfur being produced at a temperature maintained in said reaction zone between about 250° and about 475° F.; (3) recovering a first product gas stream from step (2) and separating elemental sulfur therefrom, thereby producing a first purified product gas stream, said purified product gas stream containing said residual H₂ S; (4) contacting at least some of said purified product gas stream with a solid oxidation catalyst comprising a porous refractory oxide in a second reaction zone maintained between about 250° and 900° F., said contacting being in the presence of sufficient oxygen, SO₂, or both such that a substantial proportion of said residual H₂ S is converted to elemental sulfur; and (5) recovering a second product gas stream containing elemental sulfur and separating elemental sulfur therefrom, thereby producing a second purified product gas stream.
 67. A process as defined in claim 66 wherein said catalyst in said first and second reaction zones consists essentially of more than about 7 weight percent vanadium components, calculated as V₂ O₅, and more than about 8 weight percent bismuth components, calculated as Bi₂ O₃, on a porous refractory oxide support, and wherein air is blended in step (1) and in step (4) such that essentially the stoichiometric amount of oxygen is available in said first reaction zone and essentially the stoichiometric amount of SO₂ plus O₂ is available in said second reaction zone for the conversion of H₂ S to elemental sulfur in said first and second reaction zones.
 68. A process as defined in claim 67 wherein the initial contacting in said first reaction zone is below about 400° F. and at least some conversion of H₂ S to sulfur takes place below 400° F., and wherein said feed gas stream contains sufficient water vapor that the water vapor partial pressure of said blended gas stream in step (2) is at least 4.0 p.s.i.a.
 69. A process as defined in claim 67 wherein said blended gas stream contains water vapor at a partial pressure above about 1.5 p.s.i.a.
 70. A process as defined in claim 67 wherein said blended gas stream contains water vapor at a partial pressure above about 2.0 p.s.i.a.
 71. A process as defined in claim 66 wherein said blended gas stream contains water vapor at a partial pressure of at least 4.0 p.s.i.a.
 72. A process as defined in claim 67 wherein said feed gas stream contains between about 5 and 40 volume percent H₂ S and a portion of the first purified product gas stream obtained in step (3) is recycled to step (1).
 73. A process as defined in claim 72 wherein said feed gas stream contains more than about 10 volume percent H₂ S and said recycle of said first purified product gas stream is such that the H₂ S content of the blended gas stream in step (2) is maintained at a value in the range of about 3.0 to 6.0 volume percent.
 74. A process as defined in claim 73 wherein the initial contacting in said first reaction zone is below about 400° F. and at least some conversion of H₂ S to sulfur takes place below 400° F., and wherein said feed gas stream contains sufficient water vapor that the water vapor partial pressure of said blended gas stream in step (2) is at least 4.0 p.s.i.a.
 75. A process as defined in claim 1 or 10 wherein said catalyst comprises between about 7 and 15 weight percent of vanadium components, calculated as V₂ O₅, and between about 8 and 15 weight percent of bismuth components, calculated as Bi₂ O₃.
 76. A process as defined in claim 75 wherein said catalyst is active for initiating the reaction between H₂ S and oxygen to produce sulfur at a temperature below 300° F. when a gas stream comprising water vapor at a partial pressure between about 2.5 and 5.0 p.s.i.a. and having a composition, on an anhydrous basis, comprising 99% CO₂ and between about 750 and 1200 vppm H₂ S is blended with air supplied at a rate such that oxygen is present between about 0.9 and 1.1 times the stoichiometric proportion necessary for the conversion of said H₂ S to elemental sulfur, and the resultant gases are contacted with said catalyst under the following conditions: 300 p.s.i.a. total operating pressure and a space velocity of 750 v/v/hr.
 77. A process as defined in claim 10 or 19 wherein said catalyst consists essentially of between about 7 and 15 weight percent vanadium components, calculated as V₂ O₅, and between about 8 and 15 weight percent bismuth components, calculated as Bi₂ O₃.
 78. A process as defined in claim 77 wherein said catalyst is active for initiating the reaction between H₂ S and oxygen to produce sulfur at a temperature below 300° F. when contacted with a gas stream consisting essentially of 2.0 mole percent H₂ S, 1.0 mole percent free oxygen, and about 97 mole percent nitrogen under the following conditions: about 14.7 p.s.i.a. total operating pressure and a volumetric space velocity of 29,695.5 v/v/hr.
 79. A process as defined in claim 2, 19, 30, or 54 wherein said catalyst is active for initiating the reaction between H₂ S and oxygen to produce sulfur at a temperature below 300° F. when contacted with a gas stream consisting essentially of 2.0 mole percent H₂ S, 1.0 mole percent free oxygen, and about 97 mole percent nitrogen under the following conditions: about 14.7 p.s.i.a. total operating pressure and a volumetric space velocity of 29,695.5 v/v/hr.
 80. A process as defined in claim 79 wherein at least some conversion of H₂ S to elemental sulfur is effected in the presence of said catalyst at a temperature below 325° F.
 81. A process as defined in claim 79 wherein at least some conversion of H₂ S to elemental sulfur is effected in the presence of said catalyst at a temperature below 300° F.
 82. A process as defined in claim 2, 19, or 36 wherein said catalyst is active for initiating the reaction between H₂ S and oxygen to produce sulfur at a temperature of 265° F. when contacted with a gas stream consisting essentially of 2.0 mole percent H₂ S, 1.0 mole percent free oxygen, and about 97 mole percent nitrogen under the following conditions: about 14.7 p.s.i.a. total operating pressure and a volumetric space velocity of 29,695.5 v/v/hr.
 83. A process as defined in claim 82 wherein at least some conversion of H₂ S to elemental sulfur is effected in the presence of said catalyst at a temperature below 400° F.
 84. A process as defined in claim 82 wherein at least some conversion of H₂ S to elemental sulfur is effected in the presence of said catalyst at a temperature below 300° F.
 85. A process as defined in claim 2, 19, 36, 54 or 56 wherein at least some conversion of H₂ S to elemental sulfur is effected in the presence of said catalyst at a temperature below 400° F.
 86. A process as defined in claim 2, 19, 30, 36, or 54 wherein at least some conversion of H₂ S to sulfur is effected in the presence of said catalyst at a temperature below 325° F.
 87. A process as defined in claim 2, 19, 36, or 56 wherein at least some conversion of H₂ S to sulfur is effected in the presence of said catalyst at a temperature below 300° F.
 88. A process as defined in claim 1, 10, 19, or 30 wherein said catalyst is in contact with water vapor at a partial pressure above about 75 percent of the saturation pressure and said catalyst has a mean pore diameter of 200 angstroms or more.
 89. A process as defined in claim 1, 10, 19, or 30 wherein said catalyst is in contact with water vapor at a partial pressure above about 75 percent of the saturation pressure and said catalyst has a mean pore diameter of 80 angstroms or more.
 90. A process as defined in claim 1, 2, 5, 10, 19, 24, 25 or 26 wherein at least 68.7 percent of said H₂ S is converted to elemental sulfur.
 91. A process as defined in claim 30, 37, 38, 39 or 40 wherein at least 77.0 percent of said H₂ S is reacted to produce elemental sulfur.
 92. A process as defined in claim 79 wherein at least 77.0 percent of said H₂ S is converted to elemental sulfur.
 93. A process as defined in claim 87 wherein at least 77.0 percent of said H₂ S is converted to elemental sulfur.
 94. A process as defined in claim 2 wherein said catalyst comprises about 7 to about 15 weight percent vanadium components, calculated as V₂ O₅, and about 8 to about 15 weight percent bismuth components, calculated as Bi₂ O₃, on a porous carrier material, said catalyst having a mean pore diameter of at least 200 angstroms.
 95. A process as defined in claim 1 wherein said catalyst is porous and consists essentially of vanadium and bismuth components on a carrier material, said catalyst having a mean pore diameter of at least 200 angstroms.
 96. A process as defined in claim 94 or 95 wherein said catalyst is in contact with water vapor at a partial pressure above about 75 percent of the saturation pressure. 